Magnet SmCo
| Sintered SmCoMagnetPriodweddau Corfforol | |||||||||
| Deunydd | Gradd | Remanence | Temp.-Coeff. o Br | Llu Gorfodol | Llu Gorfodol Cynhenid | Temp.-Coeff. O Hcj | Max. Cynnyrch Ynni | Max. Tymheredd Gweithredu | Dwysedd |
| Br (KGs) | Hcb (CHI) | Hcj (CHI) | (BH) max. (MGOe) | g/cm³ | |||||
| SmCo5 | XG16 | 8.1-8.5 | -0.050 | 7.8-8.3 | 15-23 | -0.30 | 14-16 | 250 ℃ | 8.3 |
| XG18 | 8.5-9.0 | -0.050 | 8.3-8.8 | 15-23 | -0.30 | 16-18 | 250 ℃ | 8.3 | |
| XG20 | 9.0-9.4 | -0.050 | 8.5-9.1 | 15-23 | -0.30 | 19-21 | 250 ℃ | 8.3 | |
| XG22 | 9.2-9.6 | -0.050 | 8.9-9.4 | 15-23 | -0.30 | 20-22 | 250 ℃ | 8.3 | |
| XG24 | 9.6-10.0 | -0.050 | 9.2-9.7 | 15-23 | -0.30 | 22-24 | 250 ℃ | 8.3 | |
| XG16S | 7.9-8.4 | -0.050 | 7.7-8.3 | ≥23 | -0.28 | 15-17 | 250 ℃ | 8.3 | |
| XG18S | 8.4-8.9 | -0.050 | 8.1-8.7 | ≥23 | -0.28 | 17-19 | 250 ℃ | 8.3 | |
| XG20S | 8.9-9.3 | -0.050 | 8.6-9.2 | ≥23 | -0.28 | 19-21 | 250 ℃ | 8.3 | |
| XG22S | 9.2-9.6 | -0.050 | 8.9-9.5 | ≥23 | -0.28 | 21-23 | 250 ℃ | 8.3 | |
| XG24S | 9.6-10.0 | -0.050 | 9.3-9.9 | ≥23 | -0.28 | 23-25 | 250 ℃ | 8.3 | |
| Sm2Co17 | XG24H | 9.5-10.2 | -0.025 | 8.7-9.6 | ≥25 | -0.20 | 22-24 | 350 ℃ | 8.3 |
| XG26H | 10.2-10.5 | -0.030 | 9.4-10.0 | ≥25 | -0.20 | 24-26 | 350 ℃ | 8.3 | |
| XG28H | 10.3-10.8 | -0.035 | 9.5-10.2 | ≥25 | -0.20 | 26-28 | 350 ℃ | 8.3 | |
| XG30H | 10.8-11.0 | -0.035 | 9.9-10.5 | ≥25 | -0.20 | 28-30 | 350 ℃ | 8.3 | |
| XG32H | 11.0-11.3 | -0.035 | 10.2-10.8 | ≥25 | -0.20 | 29-32 | 350 ℃ | 8.3 | |
| XG22 | 9.3-9.7 | -0.020 | 8.5-9.3 | ≥18 | -0.20 | 20-23 | 300 ℃ | 8.3 | |
| XG24 | 9.5-10.2 | -0.025 | 8.7-9.6 | ≥18 | -0.20 | 22-24 | 300 ℃ | 8.3 | |
| XG26 | 10.2-10.5 | -0.030 | 9.4-10.0 | ≥18 | -0.20 | 24-26 | 300 ℃ | 8.3 | |
| XG28 | 10.3-10.8 | -0.035 | 9.5-10.2 | ≥18 | -0.20 | 26-28 | 300 ℃ | 8.3 | |
| XG30 | 10.8-11.0 | -0.035 | 9.9-10.5 | ≥18 | -0.20 | 28-30 | 300 ℃ | 8.3 | |
| XG32 | 11.0-11.3 | -0.035 | 10.2-10.8 | ≥18 | -0.20 | 29-32 | 300 ℃ | 8.3 | |
| XG26M | 10.2-10.5 | -0.035 | 8.5-9.8 | 12-18 | -0.20 | 24-26 | 300 ℃ | 8.3 | |
| XG28M | 10.3-10.8 | -0.035 | 8.5-10.0 | 12-18 | -0.20 | 26-28 | 300 ℃ | 8.3 | |
| XG30M | 10.8-11.0 | -0.035 | 8.5-10.5 | 12-18 | -0.20 | 28-30 | 300 ℃ | 8.3 | |
| XG32M | 11.0-11.3 | -0.035 | 8.5-10.7 | 12-18 | -0.20 | 29-32 | 300 ℃ | 8.3 | |
| XG24L | 9.5-10.2 | -0.025 | 6.8-9.0 | 8-12 | -0.20 | 22-24 | 250 ℃ | 8.3 | |
| XG26L | 10.2-10.5 | -0.035 | 6.8-9.4 | 8-12 | -0.20 | 24-26 | 250 ℃ | 8.3 | |
| XG28L | 10.3-10.8 | -0.035 | 6.8-9.6 | 8-12 | -0.20 | 26-28 | 250 ℃ | 8.3 | |
| XG30L | 10.8-11.5 | -0.035 | 6.8-10.0 | 8-12 | -0.20 | 28-30 | 250 ℃ | 8.3 | |
| XG32L | 11.0-11.5 | -0.035 | 6.8-10.2 | 8-12 | -0.20 | 29-32 | 250 ℃ | 8.3 | |
| Nodyn: · Rydym yn aros yr un fath ag uchod oni nodir yn wahanol gan y cwsmer. Mae tymheredd Curie a chyfernod tymheredd ar gyfer cyfeirio yn unig, nid fel sail ar gyfer penderfyniad. · Mae tymheredd gweithio uchaf magnet yn newid oherwydd cymhareb hyd a diamedr a ffactorau amgylchedd. | |||||||||
Mantais:
Mae'r defnydd o'r magnetau hyn yn cael ei gyflyru gan y tymheredd mewn ystod eang sy'n rhedeg o 250ºC i 350ºC a gall eu tymheredd Curie fod mor uchel
rhwng 710 a 880 ° C. Felly, mae gan fagnet SmCo y sefydlogrwydd magnetig gorau oherwydd yr ymwrthedd uwch i dymheredd uchel.
Nodweddir magnetau SmCo gan ymwrthedd cyrydiad uchel iawn, nid oes angen cotio ar gyfer amddiffyn yr wyneb.
Nodwedd:
Anfantais magnetau SmCo yw brau amlwg y deunydd - ffactor y mae'n rhaid ei ystyried yn arbennig wrth brosesu.
Mae'r magnetau wedi'u galfanio neu eu gorchuddio gan electrodeposition cathodic ar gyfer rhai cymwysiadau.
Cais:
Mewn ardaloedd mae tymheredd gweithredu uchel, cyrydiad uchel ac ymwrthedd ocsideiddio yn hanfodol. Megis, magnetron electronig,Magnettrosglwyddo ic,
Triniaeth magnetig, Magnistor, ac ati.
Penderfynwyd ar yr holl werthoedd a nodwyd gan ddefnyddio samplau safonol yn unol â IEC 60404-5. Mae'r manylebau canlynol yn gweithredu fel gwerthoedd cyfeirio a gallant
gwahaniaethu. Yr uchafswm. tymheredd gweithredu yn dibynnu ar y dimensiwn magnet a'r cais penodol. Am fwy o wybodaeth cysylltwch â'n
peirianwyr cais.