Priodweddau Corfforol Magnet NdFeB Sintered | ||||||||
Gradd | Remanence | Temp.-Coeff. o Br | Llu Gorfodol | Llu Gorfodol Cynhenid | Temp.-Coeff. O Hcj | Max. Cynnyrch Ynni | Max. Tymheredd Gweithredu | Dwysedd |
Br (KGs) | Hcb (CHI) | Hcj (CHI) | (BH) max. (MGOe) | g/cm³ | ||||
N35 | 11.7-12.2 | -0.11~-0.12 | ≥10.9 | ≥12 | -0.58~-0.78 | 33-36 | 80 ℃ | 7.6 |
N38 | 12.2-12.5 | -0.11~-0.12 | ≥11.3 | ≥12 | -0.58~-0.78 | 36-39 | 80 ℃ | 7.6 |
N40 | 12.5-12.8 | -0.11~-0.12 | ≥11.5 | ≥12 | -0.58~-0.78 | 38-41 | 80 ℃ | 7.6 |
N42 | 12.8-13.2 | -0.11~-0.12 | ≥11.5 | ≥12 | -0.58~-0.78 | 40-43 | 80 ℃ | 7.6 |
N45 | 13.2-13.8 | -0.11~-0.12 | ≥11.6 | ≥12 | -0.58~-0.78 | 43-46 | 80 ℃ | 7.6 |
N48 | 13.8-14.2 | -0.11~-0.12 | ≥11.6 | ≥12 | -0.58~-0.78 | 46-49 | 80 ℃ | 7.6 |
N50 | 14.0-14.5 | -0.11~-0.12 | ≥10.0 | ≥12 | -0.58~-0.78 | 48-51 | 80 ℃ | 7.6 |
N52 | 14.3-14.8 | -0.11~-0.12 | ≥10.0 | ≥12 | -0.58~-0.78 | 50-53 | 80 ℃ | 7.6 |
N33M | 11.3-11.7 | -0.11~-0.12 | ≥10.5 | ≥14 | -0.58~-0.72 | 31-33 | 100 ℃ | 7.6 |
N35M | 11.7-12.2 | -0.11~-0.12 | ≥10.9 | ≥14 | -0.58~-0.72 | 33-36 | 100 ℃ | 7.6 |
N38M | 12.2-12.5 | -0.11~-0.12 | ≥11.3 | ≥14 | -0.58~-0.72 | 36-39 | 100 ℃ | 7.6 |
N40M | 12.5-12.8 | -0.11~-0.12 | ≥11.6 | ≥14 | -0.58~-0.72 | 38-41 | 100 ℃ | 7.6 |
N42M | 12.8-13.2 | -0.11~-0.12 | ≥12.0 | ≥14 | -0.58~-0.72 | 40-43 | 100 ℃ | 7.6 |
N45M | 13.2-13.8 | -0.11~-0.12 | ≥12.5 | ≥14 | -0.58~-0.72 | 43-46 | 100 ℃ | 7.6 |
N48M | 13.6-14.3 | -0.11~-0.12 | ≥12.9 | ≥14 | -0.58~-0.72 | 46-49 | 100 ℃ | 7.6 |
N50M | 14.0-14.5 | -0.11~-0.12 | ≥13.0 | ≥14 | -0.58~-0.72 | 48-51 | 100 ℃ | 7.6 |
N35H | 11.7-12.2 | -0.11~-0.12 | ≥10.9 | ≥17 | -0.58~-0.70 | 33-36 | 120 ℃ | 7.6 |
N38H | 12.2-12.5 | -0.11~-0.12 | ≥11.3 | ≥17 | -0.58~-0.70 | 36-39 | 120 ℃ | 7.6 |
N40H | 12.5-12.8 | -0.11~-0.12 | ≥11.6 | ≥17 | -0.58~-0.70 | 38-41 | 120 ℃ | 7.6 |
N42H | 12.8-13.2 | -0.11~-0.12 | ≥12.0 | ≥17 | -0.58~-0.70 | 40-43 | 120 ℃ | 7.6 |
N45H | 13.2-13.6 | -0.11~-0.12 | ≥12.1 | ≥17 | -0.58~-0.70 | 43-46 | 120 ℃ | 7.6 |
N48H | 13.7-14.3 | -0.11~-0.12 | ≥12.5 | ≥17 | -0.58~-0.70 | 46-49 | 120 ℃ | 7.6 |
N35SH | 11.7-12.2 | -0.11~-0.12 | ≥11.0 | ≥20 | -0.56~-0.70 | 33-36 | 150 ℃ | 7.6 |
N38SH | 12.2-12.5 | -0.11~-0.12 | ≥11.4 | ≥20 | -0.56~-0.70 | 36-39 | 150 ℃ | 7.6 |
N40SH | 12.5-12.8 | -0.11~-0.12 | ≥11.8 | ≥20 | -0.56~-0.70 | 38-41 | 150 ℃ | 7.6 |
N42SH | 12.8-13.2 | -0.11~-0.12 | ≥12.4 | ≥20 | -0.56~-0.70 | 40-43 | 150 ℃ | 7.6 |
N45SH | 13.2-13.8 | -0.11~-0.12 | ≥12.6 | ≥20 | -0.56~-0.70 | 43-46 | 150 ℃ | 7.6 |
N28UH | 10.2-10.8 | -0.11~-0.12 | ≥9.6 | ≥25 | -0.52~-0.70 | 26-29 | 180 ℃ | 7.6 |
N30UH | 10.8-11.3 | -0.11~-0.12 | ≥10.2 | ≥25 | -0.52~-0.70 | 28-31 | 180 ℃ | 7.6 |
N33UH | 11.3-11.7 | -0.11~-0.12 | ≥10.7 | ≥25 | -0.52~-0.70 | 31-34 | 180 ℃ | 7.6 |
N35UH | 11.8-12.2 | -0.11~-0.12 | ≥10.8 | ≥25 | -0.52~-0.70 | 33-36 | 180 ℃ | 7.6 |
N38UH | 12.2-12.5 | -0.11~-0.12 | ≥11.0 | ≥25 | -0.52~-0.70 | 36-39 | 180 ℃ | 7.6 |
N40UH | 12.5-12.8 | -0.11~-0.12 | ≥11.3 | ≥25 | -0.52~-0.70 | 38-41 | 180 ℃ | 7.6 |
N28EH | 10.4-10.9 | -0.105~-0.120 | ≥9.8 | ≥30 | -0.48~-0.70 | 26-29 | 200 ℃ | 7.6 |
N30EH | 10.8-11.3 | -0.105~-0.120 | ≥10.2 | ≥30 | -0.48~-0.70 | 28-31 | 200 ℃ | 7.6 |
N33EH | 11.3-11.7 | -0.105~-0.120 | ≥10.5 | ≥30 | -0.48~-0.70 | 31-34 | 200 ℃ | 7.6 |
N35EH | 11.7-12.2 | -0.105~-0.120 | ≥11.0 | ≥30 | -0.48~-0.70 | 33-36 | 200 ℃ | 7.6 |
N38EH | 12.2-12.5 | -0.105~-0.120 | ≥11.3 | ≥30 | -0.48~-0.70 | 36-39 | 200 ℃ | 7.6 |
N28AH | 10.4-10.9 | -0.105~-0.120 | ≥9.9 | ≥33 | -0.45~-0.70 | 26-29 | 230 ℃ | 7.6 |
N30AH | 10.8-11.3 | -0.105~-0.120 | ≥10.3 | ≥33 | -0.45~-0.70 | 28-31 | 230 ℃ | 7.6 |
N33AH | 11.3-11.7 | -0.105~-0.120 | ≥10.6 | ≥33 | -0.45~-0.70 | 31-34 | 230 ℃ | 7.6 |
Nodyn: · O dan dymheredd gweithio 20 ℃ ± 2 ℃, profir paramedrau magnetig uwch a phriodweddau ffisegol, gyda cholli grym magnetig yn anochel dim mwy na 5%. · Mae tymheredd gweithio uchaf magnet yn newid oherwydd cymhareb hyd a diamedr a ffactorau amgylchedd . |
Mantais:
Mae priodweddau'r magnetau hyn yn llawer gwell na'r rhai traddodiadol a nhw yw'r rhai mwyaf pwerus o ran eu cymhwyso ar hyn o bryd. Eu uchel
gorfodaeth a remanence uchel yn caniatáu y dyluniad newydd a'r posibilrwydd o gynyddu maes magnetig o gais lle mae gofod yn gyfyngedig
neu lle mae angen maes magnetig cryf.
Mae magnetau NdFeB yn agored iawn i gyrydiad. Felly mae angen gorchudd wyneb amddiffynnol. Mae'r defnydd o fagnet NdFeB wedi'i gyflyru
gan y tymheredd mewn ystod eang yn rhedeg o 80ºC i 230ºC. A hefyd mae'n gweithio ar dymheredd is na 0 ℃.
Cais:
Defnyddir magnetau neodymium fel gwahanol fathau o lensys magnetig ar gyfer canolbwyntio, gwyro gronynnau wedi'u gwefru mewn electroneg, systemau brêc,
drip, synhwyrydd, system magnetig mewn moduron rotor a micro, a maes gwyddoniaeth, meddygaeth (tomograffeg, sbectromedrau NMR), ac ati.
Heddiw, defnyddir magnetau NdFeB mewn symiau mawr ledled y byd. Nid yw datblygiad y deunydd hwn wedi'i gwblhau eto; y gweddillion
ac mae cryfder maes gorfodol yn cael ei gynyddu'n barhaus. Mae egni uchel magnetau NdFeB yn golygu y gellir adeiladu moduron a synwyryddion
llai fyth – ac mae hyn yn arwydd o gynnydd mewn effeithlonrwydd perfformiad. Mae'r gwelliannau parhaus yn galluogi'r deunydd diddorol hwn i barhau.
yn cael ei gyflwyno mewn meysydd newydd bob yn ail.
Penderfynwyd ar yr holl werthoedd a nodwyd gan ddefnyddio samplau safonol yn unol â IEC 60404-5. Mae'r manylebau canlynol yn gweithredu fel gwerthoedd cyfeirio a
gall fod yn wahanol. Am ragor o wybodaeth, cysylltwch â'n peirianwyr cais.